SUPERPOXY 320

Superpoxy320, has excellent resistance to continuous and alternating service for a wide range at chemicals, solvents, caustic, crude and fuel oils, animal and vegetable oils and fats, neutral, alkaline and non-oxidizing salt solutions in water.

Tank lining for shop tanks, road tankers, barges and storage tanks in the chemical and petrochemical industries.

View more

Procedure

1. Surface preparation

  • Immersion : Blast all surface in accordance with SSPC-SP5 (“White Metal”, SIS Sa 3)
  • Concrete : As a fully cured state and prepare in accordance with blast cleaning or prickling

2. Environmental Conditions

  • Over 5°C is ideal for painting and hardening.
  • The surface temperature must be at least 3°C above the dew point to prevent moisture condensation.
  • Relative humidity : up to 85%

3. Application Equipment

  • Conventional or airless spray, power mixer, brush
  • Airless spray: Tip size-0.019~0.021inch Output pressure-2200psi/150atm (*Airless spray data are indicative and subject to adjustment)
  • Recommended thinning ratio : about 10%(Airless spray)

Caution for usage

1) Mix the material according to designed mixing ratio and use after stirring it until uniformly blended. And, Use the mixed paint within pot life.

2) When used in rainy day, high humidity(Over 85%) day, low temperature(Under 10°C) condition, avoid the painting.

3) Even if you use same product(color, lot), the painting equipment and method(thinning ratio) can cause different color. So, you should check the color before using it.

4) When apply this paint to immersion region of concrete managing waterproofing, it is possible to occur peeling. So, coating work has to be proceeded after checking the adhesion with our products.

5) Don’t use this product as a floor coating.

6) When immersed before curing time for immersion service, it can make coating problems (chalking, discoloration, blistering, etc.)

7) When applied toexposed areas of outdoor, recoating time shall be within 3 days. If recoating time is passed, surface preparation by sand paper is needed to all surface and do the next coating.

8) In confined space, high humidity can make the peeling. So, ventilation is required during application and drying.

9) When apply over solvent type epoxy primer in confined space, ventilation must be required.

Safety Precautions for handling

1) Store it indoor (5~35°C) condition, avoiding heat and open flame. And, keep it standing and being closed.

2) When you dispose of it, follow the rules.

3) Use if in shelf life. Even if the shelf life passes by, it can be used after checking to our customer center. Because the paint can go deterioration and make settling.

Warning notice

Please consult our enclosed here with warning

Typical system

Preceding primer

  • (For concrete) : SUPERCRETE 820, etc.
  • (For steel, if necessary) : SUPERPOXY 130.

Standard coating system:

  • Superpoxy320, 100μm ×3coats
  • Total D.F.T 300μm

* Concrete coating system:

  • Preceding primer : Supercrete 820, 50μm
  • Superpoxy320, 125μm ×2coats
  • Total D.F.T 300μm
View more
Finish Semi-gloss
Color Grey and Light color (limit colors)
Applied over Blasted steel, primed concrete Components 2
Volume Solid About 70%
Recommended Film
Thickness 
250~300 μm
 Coats 2~3 Mixing Ratio
A : B

4:1
Theoretical Coverage 2.33m2/L (@ D.F.T. 300μm)
* Allow for application losses and surface
irregularities.
 Pot life(20°C) 1hr
Dry times(20°C) Dry through: 36hrs To topcoat(20°C) 16hrs ~ 7days
Thinner Thinner 395 Curing time for
Immersion service

9days (at 20°C)
Shelf life 12months (when stored indoor at 5 ~ 35°C)    
View more
Other Products
SUPERPOXY 1375
SUPERPOXY 1375 is a polyamide cured epoxy primer with high solids content designed for industrial and marine use in severe environmental condition. It is excellent primer in corrosive environments.
SPIPOXY FD PRIMER
SPIPOXY FD PRIMER, based on epoxy / polyamide resin, is an epoxy primer coating for industrial use with good adherence, corrosion resistance, and chemical resistance
SUPERPOXY 122LP
SUPERPOXY 122LP designed mainly on zinc polyamide epoxy primer, provides outstanding resistance to chemicals and severe weathering. This product is used as a shop primer for bare steel on new construction or major repair projects and as a field maintenance primer over bare steel or steel coated with organic or inorganic zinc primer and epoxy topcoats.
SUPERPOXY 270HB (HD)
SUPERPOXY 270HB(HD) is a high-build polyamide epoxy with high solids content designed for industrial and marine use in severe environmental condition. It provides excellent durability in marine atmosphere and economical long-term protection with only one coat.
SUPERPOXY 320GF
SUPERPOXY 320GF has excellent acid resistance to continuous and alternating service for a wide range at chemicals, solvent, caustic, crude and fuel oils, animal and vegetable oils and fats, neutral, alkaline and non-oxidizing salt solutions in water.
SUPERPOXY 360AL
SUPERPOXY 360AL is a high performance general maintenance coating that can be applied to new or old steel, requiring only the removal of loose rust and scale. It contains special ingredients that wet the surface and penetrate any existing rust.
SUPERPOXY 3230HT
SUPERPOXY 3230HT is a high density cross-linked epoxy phenolic coating suitable for protecting steelwork that is exposed to a wide range of highly corrosive environments, particularly insulated pipework subjected to wet and dry cycling, operating at temperatures up to 230°C. (Minimum temperature: -196°C) It meets CS-3, 4 for carbon steels and SS-2, 3 for stainless steels under thermal insulation according to NACE SP0198-10.
SUPERPOXY 5000NS
SUPERPOXY 5000NS used for drinking water tank interiors, is invented non solvent epoxy coating that has an excellent adhesion and durability. And it can make high dry film thickness without thinning. Also, this product suitable for KS F4921 and KC(Korea Certification).
SUPERTAR 4000
SUPERTAR 4000 is a polyamide-cured, high build coal-tar epoxy coating for non-immersion as well as immersion service, providing excellent corrosion and chemical resistance and full film thickness. It can be applied over both steel and concrete.